Solvent-resistant, compatible blends of polyphenylene ethers and linear polyesters

ABSTRACT

Impact- and solvent-resistant resin blends are prepared from a polyphenylene ether or blend thereof with a polystyrene, a linear polyester such as a poly(alkylene dicarboxylate), at least one polymer containing a substantial proportion of aromatic polycarbonate units as a compatibilizing agent, and, preferably, at least one elastomeric polyphenylene ether-compatible impact modifier. There may also be present a minor amount of at least one epoxide and/or masked isocyanate such as triglycidyl isocyanurate or a glycidyl methacrylate polymer. The polyphenylene ether preferably has a low proportion of unneutralized amino nitrogen, if any.

This application is a continuation-in-part of the following copending applications:

Ser. No. 154,751, filed Feb. 9, 1988, now U.S. Pat. No. 4,866,130;

Ser. No. 220,396, filed July 1, 1988, now abandoned;

Ser. No. 232,413, filed Aug. 15, 1988, now U.S. Pat. No. 4,978,715. Said Ser. Nos. 154,751 and 232,413 are continuations-in-part of Ser. No. 891,457, filed July 29, 1986, which is a continuation-in-part of Ser. No. 761,712, filed Aug. 2, 1985, and Ser. No. 828,410, filed Feb. 11, 1986, all now abandoned. Said Ser. No. 220,396 is a continuation of Ser. No. 10,867, filed Feb. 4, 1987, now abandoned.

This invention relates to resinous compositions having a combination of such advantageous properties as solvent resistance, high impact strength, favorable tensile properties and thermal stability. More particularly, it relates to improved polyphenylene ether compositions.

An increasing trend in recent years is the employment of resinous compositions as a replacement for metal in such areas as parts for motor vehicles. For such use, it is naturally required that the compositions have a high degree of solvent resistance, particularly to petroleum liquids such as gasoline. If exterior body parts are to be constructed of resinous compositions, they must also have very high impact strength. Other properties such as hydrolytic stability, dimensional stability, toughness, heat resistance and dielectric properties are also important in these and other areas of use.

Many of these properties are possessed by polyphenylene ethers; however, solvent resistance is not one. Therefore, it would be desirable to blend the polyphenylene ethers with resins which have a high degree of crystallinity and thus are highly resistant to solvents. Illustrative of such resins are the linear polyesters including poly(alkylene dicarboxylates), especially the poly(alkylene terephthalates). However, such blends frequently undergo phase separation and delamination. They typically contain large, incompletely dispersed polyphenylene ether particles and no phase interaction between the two resin phases. Molded parts made from such blends are typically characterized by extremely low impact strength.

The present invention provides polymer blends having a high degree of solvent resistance and other favorable properties, which may include high impact and/or tensile strength. It also provides highly compatible polymer blends containing polyphenylene ethers and poly(alkylene dicarboxylates), and resinous molding compositions suitable for use in the fabrication of automotive parts and the like.

The invention is based on the discovery of a new genus of compatible blends containing polyphenylene ethers and poly(alkylene dicarboxylates) in weight ratios as high as 1:1, or even higher under certain circumstances. According to the invention, there is also incorporated in the resinous composition a polymer containing a substantial proportion of aromatic polycarbonate structural units. Said polymer, in combination with the poly(alkylene dicarboxylate), achieves a unique and unexpected compatibilization mechanism with respect to the polyphenylene ether.

In one of its aspects, therefore, the invention is directed to resinous compositions comprising:

(A) about 15-50% of at least one polyphenylene ether, or a blend thereof with at least one polystyrene;

(B) about 20-80% of at least one poly(alkylene dicarboxylate), the weight ratio of component A to component B being at most 1.2:1; and

(C) from 3% to about 50% of at least one polymer containing a substantial proportion of aromatic polycarbonate units and having a weight average molecular weight of at least about 40,000 as determined by gel permeation chromatography relative to polystyrene, or a blend thereof with a styrene homopolymer;

all percentages being by weight and based on total components A, B and C.

It is not certain whether any or all of the components in these compositions interact chemically upon blending. Therefore, the invention includes compositions comprising said components and any reaction products thereof, as well as other optional components described hereinafter.

The polyphenylene ethers (also known as polyphenylene oxides) used as all or part of component A in the present invention are a well known class of polymers. They are widely used in industry, especially as engineering plastics in applications requiring toughness and heat resistance. Since their discovery, they have given rise to numerous variations and modifications all of which are applicable to the present invention, including but not limited to those described hereinafter.

The polyphenylene ethers comprise a plurality of structural units having the formula ##STR1## In each of said units independently, each Q¹ is independently halogen, primary or secondary lower alkyl (i.e., alkyl containing up to 7 carbon atoms), phenyl, haloalkyl, aminoalkyl, hydrocarbonoxy, or halohydrocarbonoxy wherein at least two carbon atoms separate the halogen and oxygen atoms; and each Q² is independently hydrogen, halogen, primary or secondary lower alkyl, phenyl, haloalkyl, hydrocarbonoxy or halohydrocarbonoxy as defined for Q¹. Examples of suitable primary lower alkyl groups are methyl, ethyl, n-propyl, n-butyl, isobutyl, n-amyl, isoamyl, 2-methylbutyl, n-hexyl, 2,3-dimethylbutyl, 2-, 3- or 4-methylpentyl and the corresponding heptyl groups. Examples of secondary lower alkyl groups are isopropyl, sec-butyl and 3-pentyl. Preferably, any alkyl radicals are straight chain rather than branched. Most often, each Q¹ is alkyl or phenyl, especially C₁₋₄ alkyl, and each Q² is hydrogen. Suitable polyphenylene ethers are disclosed in a large number of patents.

Both homopolymer and copolymer polyphenylene ethers are included. Suitable homopolymers are those containing, for example, 2,6-dimethyl-1,4-phenylene ether units. Suitable copolymers include random copolymers containing such units in combination with (for example) 2,3,6-trimethyl-1,4-phenylene ether units. Many suitable random copolymers, as well as homopolymers, are disclosed in the patent literature.

Also included are polyphenylene ethers containing moieties which modify properties such as molecular weight, melt viscosity and/or impact strength. Such polymers are described in the patent literature and may be prepared by grafting onto the polyphenylene ether in known manner such vinyl monomers as acrylonitrile and vinylaromatic compounds (e.g., styrene), or such polymers as polystyrenes and elastomers. The product typically contains both grafted and ungrafted moieties. Other suitable polymers are the coupled polyphenylene ethers in which the coupling agent is reacted in known manner with the hydroxy groups of two polyphenylene ether chains to produce a higher molecular weight polymer containing the reaction product of the hydroxy groups and the coupling agent. Illustrative coupling agents are low molecular weight polycarbonates, quinones, heterocycles and formals.

The polyphenylene ether generally has a number average molecular weight within the range of about 3000-40,000 and a weight average molecular weight within the range of about 20,000-80,000, as determined by gel permeation chromatography. Its intrinsic viscosity is most often in the range of about 0.15-0.6 and preferably at least 0.25 dl./g., as measured in chloroform at 25° C.

The polyphenylene ethers are typically prepared by the oxidative coupling of at least one corresponding monohydroxyaromatic compound. Particularly useful and readily available monohydroxyaromatic compounds are 2,6-xylenol (wherein each Q¹ is methyl and each Q2 is hydrogen), whereupon the polymer may be characterized as a poly(2,6-dimethyl-1,4-phenylene ether), and 2,3,6-trimethylpherol (wherein each Q¹ and one Q² is methyl and the other Q² is hydrogen).

A variety of catalyst systems are known for the preparation of polyphenylene ethers by oxidative coupling. There is no particular limitation as to catalyst choice and any of the known catalysts can be used. For the most part, they contain at least one heavy metal compound such as a copper, manganese or cobalt compound, usually in combination with various other materials.

A first class of preferred catalyst systems consists of those containing a copper compound. Such catalysts are disclosed, for example, in U.S. Pat. Nos. 3,306,874, 3,306,875, 3,914,266 and 4,028,341. They are usually combinations of cuprous or cupric ions, halide (i.e., chloride, bromide or iodide) ions and at least one amine.

Catalyst systems containing manganese compounds constitute a second preferred class. They are generally alkaline systems in which divalent manganese is combined with such anions as halide, alkoxide or phenoxide. Most often, the manganese is present as a complex with one or more complexing and/or chelating agents such as dialkylamines, alkanolamines, alkylenediamines, o-hydroxyaromatic aldehydes, o-hydroxyazo compounds, ω-hydroxyoximes (monomeric and polymeric), o-hydroxyaryl oximes and β-diketones. Also useful are known cobalt-containing catalyst systems. Suitable manganese and cobalt-containing catalyst systems for polyphenylene ether preparation are known in the art by reason of disclosure in numerous patents and publications.

The polyphenylene ethers which may be used in the invention include those which comprise molecules having at least one of the end groups of the formulas ##STR2## wherein Q¹ and Q² are as previously defined; each R¹ is independently hydrogen or alkyl, with the proviso that the total number of carbon atoms in both R¹ radicals is 6 or less; and each R² is independently hydrogen or a C₁₋₆ primary alkyl radical. Preferably, each R¹ is hydrogen and each R² is alkyl, especially methyl or n-butyl.

Polymers containing the aminoalkyl-substituted end groups of formula II may be obtained by incorporating an appropriate primary or secondary monoamine as one of the constituents of the oxidative coupling reaction mixture, especially when a copper- or manganese-containing catalyst is used. Such amines, especially the dialkylamines and preferably di-n-butylamine and dimethylamine, frequently become chemically bound to the polyphenylene ether, most often by replacing one of the α-hydrogen atoms on one or more Q¹ radicals. The principal site of reaction is the Q¹ radical adjacent to the hydroxy groups on the terminal unit of the polymer chain. During further processing and/or blending, the aminoalkyl-substituted end groups may undergo various reactions, probably involving a quinone methide-type intermediate of the formula ##STR3## with numerous beneficial effects often including an increase in impact strength and compatibilization with other blend components. Reference is made to U.S. Pat. Nos. 4,054,553, 4,092,294, 4,477,649, 4,477,651 and 4,517,341, the disclosures of which are incorporated by reference herein.

Polymers with 4-hydroxybiphenyl end groups of formula III are typically obtained from reaction mixtures in which a by-product diphenoquinone of the formula ##STR4## is present, especially in a copper-halide-secondary or tertiary amine system. In this regard, the disclosure of U.S. Pat. No. 4,477,649 is again pertinent as are those of U.S. Pat. Nos. 4,234,706 and 4,482,697, which are also incorporated by reference herein. In mixtures of this type, the diphenoquinone is ultimately incorporated into the polymer in substantial proportions, largely as an end group.

In many polyphenylene ethers obtained under the above-described conditions, a substantial proportion of the polymer molecules, typically constituting as much as about by wight of the polymer, contain end groups having one or frequently both of formulas II and III. It should be understood, however, that other end groups may be present and that the invention in its broadest sense may not be dependent on the molecular structures of the polyphenylene ether end groups.

It will be apparent to those skilled in the art from the foregoing that the polyphenylene ethers contemplated for use in the present invention include all those presently known, irrespective of variations in structural units or ancillary chemical features.

The use of polyphenylene ethers containing substantial amounts of unneutralized amino nitrogen may, under certain conditions, afford compositions with undesirably low impact and/or tensile strengths. The possible reasons for this are explained hereinafter. The amino compounds include, in addition to the aminoalkyl end groups, traces of amine (particularly secondary amine) in the catalyst used to form the polyphenylene ether.

It has further been found that the properties of the composition can often be improved in several respects, particularly impact strength, by removing or inactivating a substantial proportion of the amino compounds in the polyphenylene ether. Polymers so treated are sometimes referred to hereinafter as "inactivated polyphenylene ethers". They preferably contain unneutralized amino nitrogen, if any, in amounts no greater than 800 ppm. and more preferably in the range of about 200-800 ppm., as determined by the Kjeldahl method. Various means for inactivation have been developed and any one or more thereof may be used.

One such method is to precompound the polyphenylene ether with at least one non-volatile compound containing a carboxylic acid, acid anhydride or ester group, which is capable of neutralizing the amine compourds. This method is of particular interest in the preparation of compositions of this invention having high resistance to heat distortion. Illustrative acids, anhydrides and esters are citric acid, malic acid, agaricic acid, succinic acid, succinic anhydride, maleic acid, maleic anhyhdride, citraconic acid, citraconic anhydride, itaconic acid, itaconic anhydride, fumaric acid, diethyl maleate and methyl fumarate. Because of their relatively high reactivity with amino compounds, the free carboxylic acids and especially fumaric acid are generally most useful.

Reaction of the polyphenylene ether with the acid or anhydride may be achieved by heating at a temperature within the range of about 230°-390° C., in solution or preferably in the melt. In general, about 0.3-2.0 and preferably about 0.5-1.5 part (by weight) of acid or anhydride is employed per 100 parts of polyphenylene ether. Said reaction may conveniently be carried out in an extruder or similar equipment.

Another method of inactivation is by extrusion of the polyphenylene ether under the above-described conditions with vacuum venting. This may be achieved either in a preliminary extrusion step (which is sometimes preferred) or during extrusion of the composition of this invention, by connecting the vent of the extruder to a vacuum pump capable of reducing the pressure to about 20 torr or less.

It is believed that these inactivation methods aid in the removal by evaporation or the neutralization of any traces of free amines (predominantly secondary amines) in the polymer, including amines generated by conversion of aminoalkyl end groups to quinone methides of the type represented by formula IV. Polyphenylene ethers having a free amine nitrogen content below about 600 ppm. have been found particularly useful in this invention. However, the invention is not dependent on any theory of inactivation.

The preparation of inactivated polyphenylene ethers by reaction with acids or anhydrides, together with vacuum venting during extrusion, is illustrated by the following examples. All parts in the examples herein are by weight.

EXAMPLE 1

A mixture of 1.43 parts of maleic anhydride and 100 parts of a poly-(2,6-dimethyl-1,4-phenylene ether) having a number average molecular weight (as determined by gel permeation chromatography) of about 20,000 and an intrinsic viscosity in chloroform at 25° C. of 0.46 dl./g. was tumble-mixed for 15-30 minutes and then extruded on a 20-mm. twin screw extruder at 400 rpm. over a temperature range of about 10°-325° C. The feed rate of the mixture was about 524 grams per 10 minutes. The extruder was vacuum vented with a vacuum pump to a pressure less than 20 torr during the extrusion. The product was the desired inactivated polyphenylene ether.

EXAMPLES 2-5

The procedure of Example 1 was repeated, substituting 0.7, 0.8, 1.0 and 1.4 parts (respectively) of fumaric acid for the maleic anhydride and extruding over a temperature range of about 300°-325° C. Similar products were obtained.

EXAMPLE 6

The procedure of Example 2 was repeated, substituting 0.7 part of citric acid for the fumaric acid. A similar product was obtained.

Component A may also contain at least one polystyrene. The term "polystyrene" as used herein includes polymers prepared by methods known in the art including bulk, suspension and emulsion polymerization, which contain at least 25% by weight of structural units derived from a monomer of the formula ##STR5## wherein R³ is hydrogen, lower alkyl or halogen; Z is vinyl, halogen or lower alkyl; and p is from 0 to 5. These resins include homopolymers of styrene, chlorostyrene and vinyltoluene, random copolymers of styrene with one or more monomers illustrated by acrylonitrile, butadiene, α-methylstyrene, ethylvinylbenzene, divinylbenzene and maleic anhydride, and rubber-modified polystyrenes comprising blends and grafts, wherein the rubber is a polybutadiene or a rubbery copolymer of about 98-70% styrene and about 2-30% diene monomer. These rubber-modified polystyrenes include high impact polystyrene, or HIPS.

The proportion of polystyrene in component A is not critical, since polyphenylene ethers and polystyrenes are miscible in all proportions. Component A will generally contain about 5-50% (by weight) polystyrene, if any.

Component B is at least one linear polyester. The linear polyesters include thermoplastic poly(alkylene dicarboxylates) and alicyclic analogs thereof. They typically comprise structural units of the formula ##STR6## wherein R⁴ is a saturated divalent aliphatic or alicyclic hydrocarbon radical containing about 2-10 and usually about 2-6 carbon atoms and A¹ is a divalent aromatic radical containing about 6-20 carbon atoms. They are ordinarily prepared by the reaction of at least one diol such as ethylene glycol, 1,4-butanediol or 1,4-cyclohexanedimethanol with at least one aromatic dicarboxylic acid such as isophthalic or terephthalic acid, or lower alkyl ester thereof. The poly(alkylene terephthalates), particularly poly(ethylene terephthalate) and poly(butylene terephthalate) and especially the latter, are preferred. Such polyesters are known in the art as illustrated by the following patents:

    ______________________________________                                         2,465,319            3,047,539                                                 2,720,502            3,671,487                                                 2,727,881            3,953,394                                                 2,822,348            4,128,526.                                                ______________________________________                                    

Because of the tendency of polyesters to undergo hydrolytic degradation at the high extrusion and molding temperatures encountered by the compositions of this invention, it is preferred that the polyester used as component B be substantially free of water.

The polyesters generally have number average molecular weights in the range of about 20,000-70,000, as determined by intrinsic viscosity (IV) at 30° C. in a mixture of 60% (by weight) phenol and 40% 1,1,2,2-tetrachloroethane. When high impact strength is an important factor the polyester molecular weight should be relatively high, typically above about 40,000.

Because of the presence of both poly(alkylene dicarboxylates) and polymers containing carbonate units in the compositions of this invention, there is a possibility for ester-carbonate exchange resulting in degradation of one or both polymers, particularly at high molding temperatures. It is, therefore, sometimes preferred to incorporate in the compositions an agent which suppresses such exchange, typically in the amount of about 0.01-7.5% by weight of total polyester. It is generally preferred to precompound said exchange suppressing agent with the polyester, since it is frequently found that the impact strengths of the compositions of this invention are substantially decreased if the exchange suppressing agent is incorporated directly therein. Precompounding may be achieved by direct blending or by forming a concentrate, typically with about 1-25% by weight of the polyester, and adding said concentrate to the remaining portion thereof.

Illustrative exchange suppressing agents are hydroxyaromatic compounds such as the hydroxybenzophenones disclosed in U.S. Pat. No. 4,452,932; salicylate compounds such as methyl salicylate, disclosed in U.S. Pat. No. 4,452,933; and sodium and potassium dihydrogen phosphates disclosed in U.S. Pat. No. 4,532,290. The disclosures of all of the foregoing patents relating to polyesters are also incorporated by reference herein.

According to the present invention, the tendency of blends of components A and B to be incompatible is overcome by incorporating component C in the composition. The essential ingredient of component C is a polymer containing a substantial proportion of aromatic polycarbonate units.

Among the preferred polymers of this type are the aromatic polycarbonate homopolymers. The structural units in such homopolymers generally have the formula ##STR7## wherein A² is an aromatic radical. Suitable A² values include m-phenylene, p-phenylene, 4,4'-biphenylene, 2,2-bis(4-phenylene)propane, 2,2-bis(3,5-dimethyl-4-phenylene)propane and similar radicals such as those which correspond to the dihydroxyaromatic compounds disclosed by name or formula (generic or specific) in U.S. Pat. No. 4,217,438. Also included are radicals containing non-hydrocarbon moieties. These may be substituents such as chloro, nitro, alkoxy and the like, and also linking radicals such as thio, sulfoxy, sulfone, ester, amide, ether and carbonyl. Most often, however, all A² radicals are hydrocarbon radicals.

The A² radicals preferably have the formulas

    --A.sup.3 --Y--A.sup.4 --,                                 (IX)

wherein each of A³ and A⁴ is a monocyclic divalent aromatic radical and Y is a bridging radical in which one or two atoms separate A³ from A⁴. The free valence bcnds in formula IX are usually in the meta or para positions of A³ and A⁴ in relation to Y. Such A² values may be considered as being derived from bisphenols of the formula HO-A³ -Y-A⁴⁰ H. Frequent reference to bisphenols will be made hereinafter, but it should be understood that A² values derived from suitable compounds other than bisphenols may be employed as appropriate.

In formula IX, the A³ and A⁴ values may be unsubstituted phenylene or substituted derivatives thereof, illustrative substituents (one or more) being alkyl, alkenyl (e.g., crosslinkable-graftable moieties such as vinyl and allyl), halo (especially chloro and/or bromo), nitro, alkoxy and the like. Unsubstituted phenylene radicals are preferred. Both A³ and A⁴ are preferably p-phenylene, although both may be o- or m-phenylene or one o- or m-phenylene and the other p-phenylene.

The bridging radical, Y, is one in which one or two atoms, preferably one, separate A³ from A⁴. It is most often a hydrocarbon radical and particularly a saturated radical such as methylene, cyclohexylmethylene, 2-[2.2.1]-bicycloheptylmethylene, ethylene, 2,2-propylene, 1,1-(2,2-dimethylpropylene), 1,1-cyclohexylene, 1,1-cyclopentadecylene, 1,1-cyclododecylene or 2,2-adamantylene, especially a gem-alkylene radical. Also included, however, are unsaturated radicals and radicals which are entirely or partially composed of atoms other than carbon and hydrogen. Examples of such radicals are 2,2-dichloroethylene, carbonyl, thio and sulfone. For reasons of availability and particular suitability for the purposes of this invention, the preferred radical of formula VIII is the 2,2-bis(4-phenylene)propane radical, which is derived from bisphenol A and in which Y is isopropylidene and A³ and A⁴ are each p-phenylene.

Various methods of preparing polycarbonate homopolymers are known, and any of them may be used for preparing component C. They include interfacial and other methods in which phosgene is reacted with bisphenols, transesterification methods in which bisphenols are reacted with diaryl carbonates, and methods involving conversion of cyclic polycarbonate oligomers to linear polycarbonates. The latter method is disclosed in U.S. Pat. Nos. 4,605,731 and 4,644,053.

Copolycarbonates are also useful as component C. Examples thereof are the copolyestercarbonates of the type obtained by the reaction of at least one dihydroxyaromatic compound with a mixture of phosgene and at least one dicarboxylic acid chloride, especially isophthaloyl chloride, terephthaloyl chloride or both. Such copolyestercarbonates contain structural units of formula VIII combined with units of the formula ##STR8## wherein A⁵ is an aromatic and usually a p- or m-phenylene radical. Other examples are the siloxane-carbonate block copolymers disclosed, for example, in U.S. Pat. Nos. 3,189,662 and 3,419,634, and the polyphenylene ether-polycarbonate block copolymers of U.S. Pat. Nos. 4,374,223 and 4,436,876, which frequently provide compositions with substantially higher heat distortion temperatures than those containing homopolycarbonates. The disclosures of the patents and applications listed above relating to polycarbonates and copolycarbonates are also incorporated by reference herein.

The copolycarbonates should, for the most part, contain at least about 20% by weight of carbonate structural units. When the copolymeric units are other than ester units, the polymer preferably contains at least about 45% carbonate units.

The weight average molecular weight of the homo- or copolycarbonate should be at least about 40,000 (as determined by gel permeation chromatography relative to polystyrene). It is most often in the range of about 40,000-80,000 and especially about 50,000-80,000. However, compositions in which component C has a molecular weight in the range of about 80,000-200,000 often have favorable properties.

In most instances, component C consists of the polycarbonate or copolycarbonate; that is, said polymer is the entire component except for impurities. It is within the scope of the invention, however, to use as component C a blend of polycarbonate or copolyestercarbonate with a styrene homopolymer, typically having a number average molecular weight of about 50,000-250,000. Such blends generally contain at least 50% of the polycarbonate or copolyestercarbonate.

It is often highly preferred, according to the present invention, for the composition also to contain (D) at least one polyphenylene ether-compatible impact modifier. This is particularly true when the area of use is one which demands extremely high impact strength, such as for body parts for motor vehicles. On the other hand, impact modifiers are not necessary when impact strength is not critical but such factors as tensile properties are important; e.g., for under-hood automotive components such as electrical connectors and for internal computer parts.

Suitable impact modifiers include various elastomeric copolymers, of which examples are ethylenepropylene-diene polymers (EPDM's), both unfunctionalized and functionalized with (for example) sulfonate or phosphonate groups; ethylene-propylene rubbers, both unfunctionalized and functionalized (e.g., carboxylated); and block copolymers of alkenylaromatic compounds such as styrene with polymerizable olefins or dienes, including butadiene, isoprene, chloroprene, ethylene, propylene and butylene. Also suitable are core-shell polymers containing, for example, a poly(alkyl acrylate) core attached to a polystyrene shell via an interpenetrating network. Such core-shell polymers are more fully disclosed in U.S. Pat. No. 4,681,915.

The preferred impact modifiers are block (typically diblock, triblock or radial teleblock) copolymers of alkenylaromatic compounds and dienes. Most often, at least one block is derived from styrene and at least one other block from at least one of butadiene and isoprene. Especially preferred are the triblock copolymers with polystyrene end blocks and diene-derived midblocks. It is frequently advantageous to remove (preferably) or decrease the aliphatic unsaturation therein by selective hydrogenation. The weight average molecular weights of the impact modifiers are typically in the range of about 50,000-300,000. Block copolymers of this type are commercially available from Shell Chemical Company under the trademark KRATON, and include KRATON D1101, G1650, G1651, G1652, G1657 and G1702.

It is also appropriate to define compositions containing component D in percentage terms based on total resinous components. In those terms, the particularly preferred compositions according to this invention comprise the following, all percentage proportions being by weight of total resinous components: about 10-45% of component A; about 10-46% of component B; from 3% to about 40% of component C and about 8-25% of component D.

It will be noted that various polystyrenes may be used in the invention as all or part of components A, C and D. However, the specific polystyrenes used are different in various respects. The polystyrene in component A is a homopolymer, random copolymer or rubber-modified polystyrene; homopolymers are used in component C; and component D may be a block or core-shell copolymer. Moreover, polystyrenes are ordinarily present in only one of components A and C, if in either.

It is also within the scope of the invention to employ a polyester-aromatic polycarbonate blend as a source of part or all of components B and C. As explained hereinafter, the use of such a blend may provide somewhat more flexibility in component proportions.

Particularly in compositions containing inactivated polyphenylene ethers and relatively small amounts of polycarbonate, it is frequently found that impact strength and/or resistance to heat distortion are improved if there is also blended into the composition (E) at least one compound selected from those containing at least one cyanurate or isocyanurate moiety and those containing a plurality of epoxide moieties. Illustrative cyanurates and isocyanurates are cyanuric chloride, triethyl cyanurate, triallyl cyanurate, triallyl isocyanurate and triphenyl cyanurate. Epoxide compounds include homopolymers of such compounds as glycidyl acrylate and glycidyl methacrylate, as well as copolymers thereof, preferred comonomers being lower alkyl acrylates, methyl methacrylate, acrylonitrile and styrene. Also useful are epoxy-substituted cyanurates and isocyanurates such as triglycidyl cyanurate and triglycidyl isocyanurate.

In various respects, the proportions of ingredients in the compositions of this invention are an important consideration. It is generally contemplated that components A and B will be present in the compositions described hereinabove in the amounts of about 15-50% and 20-80% respectively, based on total components A, B and C. The preferred proportions of components A and B are in the ranges of about 20-45% and about 20-75%, respectively. Moreover, the weight ratio of component A to component B should be at most 1.2:1, since if component A is present in greater amounts the impact strength of the composition may decrease sharply. Said weight ratio is preferably about 0.7-1.0:1. When employed, the impact modifier (component D) is present in amounts up to about 35% and preferably in the range of about 10-25%, based on the total of components A, B and C. In terms of total resinous components, it is generally contemplated to employ about 10-45% and preferably about 15-45% of each of components A and B, and about 8-25% and preferably about 10-20% of component D.

With respect to the proportion (based on components A, B and C) of component C, the compatibilizing polymer, the invention includes three major embodiments although species outside these embodiments are also contemplated. The first embodiment includes compositions containing about 15-45% of component C. In such compositions, component A is typically a polyphenylene ether which has not been inactivated. Levels of components A, B and C of about 20-40%, 30-45% and 25-45% (respectively), based on the total of components A, B and C, are usually preferred in such compositions for maximum ductility. More preferably, compositions of the first embodiment comprise the following, percentages being based on total resinous components: about 15-35% of polyphenylene ether as component A, about 10-35% of component B, about 10-40% and most often about 20-40% of component C and from 8% to about 25% of component D.

When component A is not inactivated and components B and C are supplied in full or in part by a polyester-aromatic polycarbonate blend, it is frequently possible to attain the desired high impact strengths by using proportions of certain components outside of those previously described. This is true in at least two respects: the possibility of using a lower proportion of component B with respect to component A, and of employing more than 40% of component C. Thus, another aspect of the present invention is compositions comprising (based on total resinous components) about 15-35% of polyphenylene ether as component A, about 10-35% of component B, from 12% to about 50% of at least one aromatic polycarbonate as component C and about 10-25% of component D; with the provisos that all of component B and at least about 60% of component C are supplied as a poly(alkylene dicarboxylate)-aromatic polycarbonate blend, and that the weight ratio of component A to component B is at most about 1.8:1 and preferably about 0.7-1.8:1.

In the second embodiment, component A is an inactivated polyphenylene ether and the proportions of components A and B are each about 35-55%, based on the total of components A, B and C. The proportion of component C is about 5-15%, and the blend may also include component D and component E, the latter in the amount of about 0.15-3.5 and preferably at least about 0.4 part per 100 parts of total components A, B and C). Most preferably according to this embodiment, the compositions contain about 30-45% each of components A and B and about 3-10% of component C, all based on total resinous components, and component E in the amount of about 0.1-3.0 and most desirably at least about 0.25 part per 100 parts of components A, B, C and D taken together. This embodiment is often characterized by relatively high heat distortion temperatures.

It is within the scope of this second embodiment to introduce component E by blending with the other components in a single blending operation. However, it is often preferred to premix component E with component B, typically by dry mixing followed by preextrusion. Such premixing increases the melt viscosity of component B, probably by increasing molecular weight, and frequently also increases the impact strength of the composition of the invention.

In the third embodiment, component A is an inactivated polyphenylene ether and the polycarbonate has a weight average molecular weight in the range of about 80,000-200,000, preferably about 150,000-200,000. Compositions in which these polycarbonates and other components are present in the same proportions as in the second embodiment are generally characterized by high impact strengths even when component E is absent.

The chemical roles of the inactivated polyphenylene ether and of component E in the compositions of this invention are not fully understood, and any reliance on chemical theory as a basis for the invention is specifically disclaimed. It is believed, however, that the presence of more than a certain minimum proportion of amino compounds in the polyphenylene ether can cause degradation in the molecular weight of the polycarbonate and/or polyester. Such amino compounds include, in addition to the aminoalkyl end groups, traces of amines (particularly secondary amine) in the catalyst used to form the polyphenylene ether. If this is true, the removal or neutralization of the greater part of such amino compounds produces an environment in which high molecular weight is maintained in the polycarbonate, thus maximizing its effect as a compatibilizing agent, and/or in the polyester.

The compositions of this invention have been shown by scanning electron microscopy to consist essentially of particles of polyphenylene ether (component A) dispersed in a continuous polyester-containing phase. The size and shape of said particles varies with such factors as the proportion of polyphenylene ether in the composition. The elastomeric impact modifier (component D), when present, is substantially entirely in the disperse phase. Component C is present in the continuous phase and improves the ductility thereof; it also forms a "coating" around the dispersed polyphenylene ether particles and provides good adhesion of said particles to the continuous phase. By reason of the size and shape of the disperse phase particles and/or their degree of adhesion to the continuous phase as a result of the action of component C, the compositions are highly resistant to delamination and similar types of failure under stress.

It is within the scope of the invention for the composition to contain other conventional ingredients such as fillers, flame retardants, pigments, dyes, stabilizers, antistatic agents, mold release agents and the like. The presence of other resinous components is also contemplated. These include impact modifiers compatible with component B, such as various graft and core-shell copolymers of such monomers as butadiene, styrene, butyl acrylate and methyl methacrylate. It is frequently preferred to preextrude such impact modifiers with component B, optionally in admixture with component C, prior to its utilization in the invention. By this method, compositions having improved ductility at low temperatures may be prepared.

Also included as other resinous components are other impact and processability modifiers for component A, such as olefin copolymers. In general, the amounts of any other resinous components, if present, will not exceed about 15% by weight of total resin.

The preparation of the compositions of this invention is normally achieved by merely blending the ingredients thereof under conditions adapted for the formation of an intimate blend. Such conditions often include extrusion, which may be conveniently effected in a screw-type or similar extruder which applies a substantial shearing force to the composition, thereby decreasing the particle size thereof. The extrusion temperature is generally in the range of about 100°-325° C. over the length of the extruder.

The extrusion conditions may affect the impact strength and other properties of the composition. For example, it is sometimes found that the impact strength of the composition is increased if it is extruded more than once, thereby insuring effective blending.

In another embodiment, a single extruder is employed which has at least two ports for introduction of ingredients, one such port being downstream from the other. Component A or any reactants for preparation thereof and at least a portion of component D are introduced through the first port and extruded, preferably at a temperature in the range of about 300°-350° C. This portion of the extruder is preferably vacuum vented.

The remaining ingredients are introduced through the downstream port and extrusion is continued, preferably at a lower temperature to minimize degradation of components B and D. For further minimization of degradation, it may be advantageous to introduce a portion of component D at this point. Typical extrusion temperatures at this stage are in the range of about 260°-320° C.

In the following examples illustrating the inventions, the blend constituents used were as follows:

Component A

PPE--a poly(2,6-dimethyl-1,4-phenylene ether) having a number average molecular weight of about 20,000 and an intrinsic viscosity in chloroform at 25° C. of 0.46 dl./g; it was found to contain about 1000 ppm. nitrogen.

Example 1, etc.--the products of the designated examples. The product of Example 2 contained about 600 ppm. nitrogen.

Example 2 (etc )-NVV--a product similar to that of Example 2 (etc.) but prepared with atmospheric rather than vacuum venting.

PPE-VV--PPE which has been extruded on a twin screw extruder within the temperature range of about 300°-315° C., with vacuum venting to a maximum pressure of 20 torr; it contained 438 ppm. nitrogen.

HIPS--American Hoecht 1897 rubber-modified polystyrene.

Component B

PBT(50,000) and PBT(25,000)--poly(butylene terephthalates) having number average molecular weights, as determined by gel permeation chromatography, of about 50,000 and 25,000, respectively.

PBT-ES--PBT(50,000) containing NaH₂ PO₄ as an exchange-suppressing agent. The NaH₂ PO₄ was preblended with a portion of the polyester to a level of 1.8% by weight, after which 20% of said polyester was blended with untreated polyester.

PET(28,000) and PET(45,000)--poly(ethylene terephthalates) having number average molecular weights of about 28,000 and 45,000, respectively, as determined from intrinsic viscosity at 30° C. in a 3:2 (by weight) mixture of phenol and 1,1,2,2-tetrachloroethane.

Component C

PC(43,000), PC(50,000), PC(71,000), PC(192,000)--bisphenol A homopolycarbonates prepared interfacially and having weight average molecular weights of about 43,000, 50,000, 71,000 and 192,000, respectively.

PC-Trans--a bisphenol A homopolycarbonate prepared by transesterification of diphenyl carbonate and having a weight average molecular weight of about 37,000.

SH-PC--a 2,2-bis(3,5-dimethyl-4-hydroxyphenyl)propane polycarbonate prepared interfacially and having a weight average molecular weight of about 50,000.

Allyl-PC--a copolycarbonate of 97.3 mole percent bisphenol A and 2.7 mole percent 2,2-bis(3-allyl-4-hydroxyphenyl)propane, prepared interfacially and having a weight average molecular weight of about 47,000.

PPE-PC--a block poly(2,6-dimethyl-1,4-phenylene ether)-bisphenol A polycarbonate copolymer in which the two blocks have approximately equal molecular weights.

PE-PC--a polyester-polycarbonate containing 78 mole percent polyester and 22 mole percent polycarbonate units and having a weight average molecular weight of about 50,000, prepared by the interfacial reaction of bisphenol A with phosgene and a 93:7 (by weight) mixture of isophthaloyl and terephthaloyl chloride.

PC-SIL--a block copolymer containing 76% bisphenol A polycarbonate units and 24% poly(dimethylsiloxane) units, having a weight average molecular weight of about 50,000.

PS--a commercially available styrene homopolymer having a number average molecular weight of about 106,000 and an intrinsic viscosity in toluene at 25° C. of 0.80 dl./g.

Component D

SEBS--a commercially available triblock copolymer with polystyrene end blocks having weight average molecular weights of 29,000 and a hydrogenated butadiene midblock having a weight average molecular weight of 116,000.

SBS--a triblock copolymer similar to SEBS but containing an unhydrogenated butadiene midblock.

SB(H)--a styrene butadiene diblock copolymer having weight average molecular weight of about 164,00 and a butadiene-styrene weight ratio of about 2:1, in which the butadiene block has been hydrogenated.

CS--a core-shell polymer with a poly(butyl acrylate) core and polystyrene shell, connected via an interpenetrating network.

Component E

TGIC--triglycidyl isocyanurate.

GMA--a glycidyl methacrylate homopolymer having an intrinsic viscosity in chloroform at 25° C. of 0.16.

GMA-AA(15) and GMA-AA(30)--commercially available terpolymers of glycidyl methacrylate, methyl methacrylate and a lower alkyl acrylate, respectively containing 15% and 30% (by weight) glycidyl methacrylate units and having weight average molecular weights of about 11,400 and 9,000.

GMA-M--a commercially available copolymer of glycidyl methacrylate (50% by weight) and styrene, having a weight average molecular weight of about 11,000.

GMA-S-M--a commercially available terpolymer of glycidyl methacrylate (50% by weight), styrene and methyl methacrylate, having a weight average molecular weight of about 10,000.

GMA-S-A(10A), GMA-S-A(10B), GMA-S-A(20)--commercially available terpolymers of glycidyl methacrylate, styrene and acrylonitrile, respectively containing 10%, 10% and 20% (by weight) glycidyl methacrylate and having weight average molecular weights of about 8,700, 50,000 and 8,100.

All proportions in the examples are by weight. Impact and tensile values were determined in British units and have been converted to metric units. Heat distortion temperatures were determined by ASTM procedure D648, at 0.455 MPa. unless otherwise indicated.

EXAMPLES 7-13

A series of compositions according to the invention was prepared by tumble mixing the ingredients in a jar mill for 1/2 hour and extruding at 120°-287° C. on a twin screw extruder at a screw speed of 400 rpm. The extrudates were quenched in water and pelletized. The pellets were then injection molded into test bars which were evaluated for notched Izod impact strength according to ASTM procedure D256. (An impact strength greater than about 105 joules/m. is generally an indication of suitability as a molding composition, and a value above about 550 is exceptional.) The fracture surfaces of the Izod test bars were inspected for delamination and none was detected.

The relevant parameters and test results are given in Table I.

                  TABLE I                                                          ______________________________________                                                   Example                                                                        7    8      9      10   11   12   13                                 ______________________________________                                         Component A: PPE,                                                                          21     27     25   25   21   21   21                               parts                                                                          Component B, parts:                                                            PBT(50,000) 29     27     25   25   --   --   29                               PET(28,000) --     --     --   --   29   --   --                               PET(45,000) --     --     --   --   --   29   --                               Component C:                                                                               36     33     31   31   36   36   36                               PC(50,000), parts                                                              Component D,                                                                   parts:                                                                         SEBS        14     13     19   --   14   14   --                               SI(H)       --     --     --   19   --   --   --                               SBS         --     --     --   --   --   --   14                               Izod impact 603    160    609  550  198  278  598                              strength, joules/m.                                                            ______________________________________                                    

The heat distortiOn temperature of the product of Example 7 was 106° C. (83° C. at 1.82 MPa.).

EXAMPLE 14

The effect of multiple extrusions and the solvent resistance of a blend identical in composition to that of Example 7 were tested. After one extrusion, the blend had an Izod impact strength of 454 joules/m.; upon extrusion a second time, the impact strength was increased to 641 joules/m.

In a solvent resistance test, the test specimen having an impact strength of 641 joules/m. was immersed in gasoline for two days under stress. It was then found to have an impact strength of 214 joules/m., which is still a respectably high figure. No signs of dissolution or deterioration were noted.

EXAMPLES 15-20

The procedure of Example 7 was repeated, using other resins as components B and C. The relevant parameters and results are given in Table II. No delamination of any specimen was observed.

                  TABLE II                                                         ______________________________________                                                      Example                                                                        15   16     17     18   19   20                                   ______________________________________                                         Component A: PPE, parts                                                                       28     28     31   31   34   34                                 Component B: PBT-ES,                                                                          28     28     31   31   34   34                                 parts                                                                          Component C, parts:                                                            PC(50,000)     25     --     19   --   12   --                                 PC(71,000)     --     25     --   19   --   12                                 Component D: SEBS,                                                                            19     19     19   19   19   19                                 parts                                                                          Izod impact strength,                                                                         625    801    694  790  139  112                                joules/m.                                                                      Heat distortion temp., °C.                                                             111    --     --   --   127  --                                 ______________________________________                                    

EXAMPLES 21-28

The procedure of Example 7 was repeated, using other resins as components B, C and D. The relevant parameters and test results are given in Table III. No delamination of any specimen was observed.

                                      TABLE III                                    __________________________________________________________________________                   Example                                                                         21 22 23 24 25 26 27 28                                         __________________________________________________________________________     Component A: PPE, parts                                                                       21 21 21 28 21 34 31 28                                         Component B: PBT-ES, parts                                                                    29 29 29 28 29 34 31 28                                         Component C, parts:                                                            PC(43,000)     36 -- -- -- -- -- -- --                                         SH-PC          -- 36 18 -- -- -- -- --                                         PE-PC          -- -- -- -- 36 -- -- --                                         PPE-PC         -- -- -- -- -- 12 25 25                                         PC-SIL         -- -- -- 25 -- -- -- --                                         PS             -- -- 18 -- -- -- -- --                                         Component D: SEBS, parts                                                                      14 14 14 19 14 19 13 19                                         Izod impact strength,                                                                         176                                                                               278                                                                               182                                                                               449                                                                               251                                                                               117                                                                               764                                                                               732                                        joules/m.                                                                      Heat distortion temp., °C.                                                             -- -- -- -- 97 150                                                                               157                                                                               149                                        __________________________________________________________________________

Referring Specifically to Examples 26-27 in comparison with Example 19, and Example 28 in comparison with Example 15, it will be seen that compositions containing block polyphenylene ether-polycarbonates have substantially higher heat distortion temperatures than those containing homopolycarbonates, as well as equivalent or higher impact strengths.

EXAMPLES 29-31

Following the procedure of Example 7, blends were prepared in which component B was provided entirely and component C entirely or partially by a polyester-polycarbonate blend containing 39% PBT-ES, 49% PC(50,000), 8.5% of a commercial butadiene-styrene-methyl methacrylate graft copolymer and 3.5% of various fillers and stabilizers.

The relevant parameters and results are given in Table IV. No delamination of any specimen was observed.

                  TABLE IV                                                         ______________________________________                                                            Example                                                                        29    30      31                                            ______________________________________                                         Polyester-polycarbonate blend, parts                                                                64      32      50                                        Polycarbonate, parts --      32      14                                        Component A, parts   21.7    21.5    21.6                                      Component B, parts   25.8    12.7    20.0                                      Component C, parts   32.4    48.7    39.6                                      Component D, parts   14.5    14.3    14.4                                      Graft copolymer, parts                                                                              5.6     2.8     4.4                                       Izod impact strength, joules/m.                                                                     481     529     534                                       ______________________________________                                    

EXAMPLES 32-34

Compositions were prepared according to the procedure of Example 7, except that the extrusion temperature range was 120°-260° C. In these compositions, component A was the product of Example 1 and the other components were as listed in Table V. TGIC was also present in Examples 33 and 34.

Test bars were molded and evaluated for notched Izod impact strength, heat distortion temperature and tensile properties (ASTM procedure D638). The relevant parameters and test results are also given in Table V.

                  TABLE V                                                          ______________________________________                                                           Example                                                                        32    33       34                                            ______________________________________                                         Component A: Example 1, parts                                                                      40      41.4     40                                        Component B: PBT(50,000), parts                                                                    40      41.4     40                                        Component C: PC(50,000), parts                                                                     8       8.1      8                                         Component D: SEBS, parts                                                                           12      9.1      12                                        Component E: TGIC, parts                                                                           --      0.5      0.8                                       Izod impact strength, joules/m.                                                                    107     166      267                                       Heat distortion temp., °C.                                                                  --      166      156                                       Tensile strength at yield, MPa.                                                                    44.9    --       46.0                                      Tensile elongation, %                                                                              45      --       58                                        ______________________________________                                    

EXAMPLE 35

Test bars of the composition of Example 34 were immersed in gasoline for three days under stress. At the end of this time, the Izod impact strength was 155 joules/m., the tensile strength at yield was 27.1 MPa., and the tensile elongation was 20%. Upon immersion of similar test bars in water at room temperature or at its boiling point for three days, and upon aging at 80° C. for one week, weight and dimensional changes substantially less than 1% were observed.

EXAMPLES 36-43

Following the procedure of Example 32, compositions were prepared from the product of Example 3 and its atmospherically vented counterpart. The relevant parameters and test results are given in Table VI.

                                      TABLE VI                                     __________________________________________________________________________                    Example                                                                        36  37  38  39  40  41  42  43                                  __________________________________________________________________________     Component A, parts:                                                            Example 3      40  40  40  40  42  40  40  --                                  Example 3-NVV  --  --  --  --  --  --  --  40                                  Component B, parts:                                                            PBT(50,000)    40  40  40  40  42  --  40  40                                  PBT(25,000)    --  --  --  --  --  40  --  --                                  Component C, parts:                                                            PC(50,000)     8   8   8   --  --  --  8   8                                   PC(71,000)     --  --  --  8   4   8   --  --                                  Component D, parts:                                                            SEBS           12  12  12  12  12  12  --  12                                  SB(H)          --  --  --  --  --  --  12  --                                  Component E: TGIC, parts                                                                      0.8 0.32                                                                               0.5 0.8 0.8 0.8 0.8 0.8                                 Izod impact strength,                                                                         790 673 828 806 395 192 219 155                                 joules/m.                                                                      Heat distortion temp., °C.                                                             177 148 175 158 --  156 172 --                                  Tensile strength at yield,                                                                    46.9                                                                               47.9                                                                               50.1                                                                               46.9                                                                               --  45.5                                                                               47.6                                                                               --                                  MPa.                                                                           Tensile elongation, %                                                                         96  54  106 69  --  48  40  --                                  __________________________________________________________________________

EXAMPLE 44

Test bars of the composition of Example 36 were immersed in gasoline for four days under stress. At the end of this time, the Izod impact strength was 769 joules/m., the tensile strength at yield was 33.9 MPa. and the tensile elongation was 144%.

EXAMPLES 45-48

Following the procedure of Example 32, compositions were prepared in which components A, C and D varied in additional respects. The relevant parameters and test results are given in Table VII.

                  TABLE VII                                                        ______________________________________                                                           Example                                                                        45   46     47      48                                       ______________________________________                                         Component A, parts:                                                            Example 6           40     --     --    --                                     PPE-VV              --     40     40    40                                     Component B: PBT(50,000), parts                                                                    40     40     40    40                                     Component C, parts:                                                            PC(50,000)          8      8      --    8                                      PC(192,000)         --     --     8     --                                     Component D, parts:                                                            SEBS                12     12     12    --                                     CS                  --     --     --    12                                     Component E: TGIC, parts                                                                           0.8    0.5    --    0.5                                    Izod impact strength, joules/m.                                                                    785    769    764   486                                    Heat distortion temperature, °C.                                                            --     167    --    --                                     ______________________________________                                    

EXAMPLES 49-51

Following the procedure of Example 32, compositions were prepared using as components B and C the following preextruded blend:

PBT(50,000): 69.55%

PC(50,000): 15%

PBT impact modifier: 15%

Stabilizers, exchange suppressor: 0.45%.

The PBT impact modifier was "KM-330", a poly(butyl acrylate)-poly(methyl methacrylate) core-shell polymer commercially available from Rohm & Haas Company.

The parameters and test results for Examples 49-51 are given in Table VIII.

                  TABLE VIII                                                       ______________________________________                                                         Example                                                                        49     50       51                                             ______________________________________                                         Component A, parts:                                                            Example 3         36.6     --       --                                         PPE-VV            --       36.6     36.6                                       Component B, parts                                                                               36.4     36.4     36.4                                       Component C, parts                                                                               7.9      7.9      7.9                                        Component D: SEBS, parts                                                                         11.2     11.2     11.2                                       Component E: TGIC, parts                                                                         0.4      0.4      --                                         KM-330, parts     7.9      7.9      7.9                                        Izod impact strength, joules/m.                                                                  721      192      198                                        ______________________________________                                    

EXAMPLE 52

A twin screw extruder with two vacuum vents and two charging ports, one downstream from the other, was used. The first port was charged with 30 parts of PPE, 14 parts of SEBS and minor proportions of stabilizers and pigments. These materials were extruded at temperatures in the range of about 315°-350° C. and pressures in the range of about 150-205 torr. These were added through the downstream port 46 parts of PBT(50,000) and 10 parts of PC(71,000), and extrusion was continued at temperatures in the range of 260°-315° C. and pressures of about 635 torr. The extrudate was the desired product.

EXAMPLES 53-56

Following the procedure of Example 32, compositions were prepared in which various polycarbonates were used as component D. The relevant parameters and test results are given in Table IX.

                  TABLE IX                                                         ______________________________________                                                          Example                                                                        53   54      55     56                                        ______________________________________                                         Component A, parts:                                                            PPE-VV             40     --      --   --                                      Example 2          --     40      40   40                                      Component B: PBT(50,000), parts                                                                   40     40      40   40                                      Component C, parts:                                                            PC-Trans           8      8       8    --                                      Allyl-PC           --     --      --   8                                       Component D: SEBS, parts                                                                          12     12      12   12                                      Component E: TGIC, parts                                                                          --     --      0.5  --                                      Izod impact strength, joules/m.                                                                   182    256     828  278                                     ______________________________________                                    

EXAMPLES 56-67

Following the procedure of Example 32, compositions were prepared containing 40 parts of the inactivated polyphenylene ether of Example 3, 40 parts of PBT(50,000), 12 parts of SEBS, 8 parts of PC(50,000) and, as component E, various materials. The identity of these materials and the test results are given in Table X.

                  TABLE X                                                          ______________________________________                                                                     Tensile                                                               Izod     strength Tensile                                   Component E        impact   at       elong-                                    Ex-                Amt.,   strength                                                                              break  ation,                                ample Identity     parts   joules/m.                                                                             MPa.   %                                     ______________________________________                                         57      --         --      219    38.8   45                                    58    TGIC         0.8     673    42.7   78                                    59    GMA          1.0     764    42.8   71                                    60    GMA-AA(15)   1.0     657    41.7   50                                    61    GMA-AA(30)   1.0     678    43.8   66                                    62    GMA-S-M      1.0     609    47.9   79                                    63    GMA-S        1.0     710    46.5   98                                    64    GMA-M        1.0     587    48.2   86                                    65    GMA-S-A(10A) 1.0     657    41.4   53                                    66    GMA-S-A(10B) 1.0     684    40.2   49                                    67    GMA-S-A(20)  1.0     646    43.2   65                                    ______________________________________                                    

The results in Table X show the improvement in impact strength which results from the incorporation of various species of component E in the compositions of this invention. Such compositions containing component E also have high impact strengths at low temperatures. For example, the composition of Example 67 had an Izod impact strength at -40° C. of 198 joules/m.

EXAMPLES 68-70

Blends similar to those of Examples 57-67 were prepared, substituting PPE-VV for the product of Example 2. The results are given in Table XI.

                  TABLE XI                                                         ______________________________________                                         Component E          Izod impact                                               Example Identity   Amt., parts                                                                              strength, joules/m.                               ______________________________________                                         68      --         --        294                                               69      GMA        1.0       680                                               70      GMA-M      1.0       660                                               ______________________________________                                    

EXAMPLES 71-75

These examples show the effect on polyester melt viscosity of premixing the polyester with component E, the proportions of the latter being percentages by weight of polyester. Premixing was effected by dry blending followed by melt extrusion. The melt viscosities, or, in some cases, melt flow rates (which are inversely proportional to melt viscosities) were compared with those of controls which had been similarly extruded without the addition of component E. The melt viscosity of the polyester before extrusion was about 7,500 poises.

The relative parameters and test results are given in Table XII.

                  TABLE XII                                                        ______________________________________                                                               Melt     Melt                                            Component E           viscosity,                                                                              flow rate,                                      Example Identity    Amt., %   poises g./10 min.                                ______________________________________                                         Controls                                                                                 --        --          5,900                                                                               38.7                                      71      TGIC        0.5         41,000                                                                              --                                        72      TGIC        1.0       >135,000                                                                              --                                        73      GMA         1.0       --     5.0                                       74      GMA-M       1.0       --     3.4                                       75      GMA-S-A(20) 1.0       --     4.5                                       ______________________________________                                    

EXAMPLES 76-79

Following the procedure of Example 32, compositions were prepared containing 40 parts of the inactivated polyphenylene ether of Example 2, 40 parts of poly(butylene terephthalate) which had been premixed with TGIC as described in Examples 71-75, 12 parts of SEBS and 8 parts of PC(50,000). They were compared with Controls I and II prepared from untreated poly(butylene terephthalates), and Control III, wherein the TGIC was dry blended with all of the other components. The relative parameters and test results are given in Table XIII.

                                      TABLE XIII                                   __________________________________________________________________________             Example                     Control                                            76     77     78     79     I      II     III                          __________________________________________________________________________     Component B,                                                                           25,000 25,000 25,000 50,000 25,000 50,000 25,000                       mol. wt.                                                                       Component E                                                                    (TGIC):                                                                        % based on                                                                             0.5    1.0    2.0    0.5     0      0     --                           polyester                                                                      Amt. in blend,                                                                         0.2    0.4    0.8    0.2    --     --     0.8                          parts                                                                          Izod impact                                                                            224    256    570    500    80     220    192                          strength,                                                                      joules/m                                                                       __________________________________________________________________________

EXAMPLE 80

This example demonstrates the effect on impact strength of nitrogen content and molecular weight of the polyphenylene ether. Blends similar to that of Example 32 were prepared by the procedure described therein, using as component C two different bisphenol A polycarbonates prepared interfacially and as component A a number of polyphenylene ethers prepared by procedures which did not include functionalization or vacuum venting. Components B and D were PBT(50,000) and SEBS, respectively. The results are given in Table XIV.

                  TABLE XIV                                                        ______________________________________                                                                          Izod                                          Polyphenylene ether     Polycar- impact                                        IV,                     bonate   strength,                                     dl./g.  Nitrogen, ppm.  mol. wt. joules/m.                                     ______________________________________                                         0.46    1020            50,000   20                                            0.40    1115            "        20                                            0.29    497             "        78                                            0.18    353             "        22                                            0.53    576             "        57                                            0.46    1020            71,000   26                                            0.40    1115            "        26                                            0.29    497             "        115                                           0.18    353             "        22                                            0.53    576             "        265                                           ______________________________________                                    

It will be seen that comparatively high impact strengths are obtained by using a polyphenylene ether having a nitrogen content no greater than 800 ppm. and an intrinsic viscosity of at least 0.25 dl./g.

EXAMPLE 81

This example shows the effect of fumaric acid level in the inactivated polyphenylene ether on the impact strengths of the compositions. The procedure of Example 32 was employed to prepare compositions from 40 parts of various fumaric acid-inactivated polyphenylene ethers, 40 parts of PBT(50,000), 12 parts of SEBS, 8 parts of PC(50,000) and, in certain cases, 0.32 part of TGIC. The impact strengths of the compositions are given in Table XV.

                  TABLE XV                                                         ______________________________________                                                      Fumaric            Impact strength,                               Polyphenylene ether                                                                         acid level*                                                                              TGIC     joules/m.                                      ______________________________________                                         Ex. 2        0.7       No       155                                            Ex. 4        1.0       No       198                                            Ex. 5        1.4       No       294                                            Ex. 2        0.7       Yes      700                                            Ex. 4        1.0       Yes      774                                            Ex. 5        1.4       Yes      726                                            ______________________________________                                          *Parts per 100 parts of polyphenylene ether.                             

It is apparent that increasing levels of fumaric acid result in substantial increases in impact strength in the absence of component E. The presence of component E inherently causes such a profound increase in impact strength that the effect of fumaric acid level becomes insignificant.

EXAMPLES 82-84

Formulations having the weight ratios indicated in Table XVI were prepared by blending and extrusion of the components on a Werner-Pfleiderer twin screw extruder.

The extruder had two stages. The PPE, polystyrene and half the SEBS were fed to the extruder at its throat in order to ensure intimate mixing. This first stage of the extruder had a set temperature of about 350° to 360° C. and vacuum was applied to the melt. The PBT, PC and remaining SEBS were fed downstream at the second stage of the extruder which had a set temperature of about 240° to 250° C. This second stage provided adequate shear mixing of the components while avoiding potential degradation of the components due to exposure to high temperatures for longer periods.

The extrudates were quenched in water and pelletized. The pellets were then injection molded into test specimens which were evaluated for heat distortion temperature, flow channel, Dynatup impact, notched Izod impact and tensile yield and elongation. Test results are given in Table XVI.

                  TABLE XVI                                                        ______________________________________                                         Examples            82       83     84                                         ______________________________________                                         Component A, parts:                                                            PPE                 31.3     28.3   28.3                                       Polystyrene homopolymer                                                                            --       9.4    --                                         HIPS                --       --     9.4                                        Component B: PBT(50,000), parts                                                                    47.9     43.4   43.4                                       Component C: PC(71,000), parts                                                                     8.3      7.6    7.6                                        Component D: SEBS, parts                                                                           12.5     11.3   11.3                                       Heat distortion temperature, °C.                                                            147      154    150                                        Flow channel, cm.   39.4     53.3   48.3                                       Dynatup impact, joules                                                         Room temperature    44.7     51.5   52.9                                       -29° C.      47.5     50.2   56.9                                       Izod impact strength, joules/m.                                                                    828      662    651                                        Tensile strength at yield, MPa.                                                                    41.4     47.6   50.3                                       Tensile elongation, %                                                                              43       29     29                                         ______________________________________                                    

EXAMPLES 85-88

In this series of examples, blends were prepared in the same manner as described above for Examples 82-84. The weight ratio of the polyphenylene ether to polystyrene was varied. In this series, component B was PBT(50,000), (45 parts), component C was PC(71,000) (8 parts) and component D was SEBS (12 parts). Table XVII indicates the manner in which the polyphenylene ether and the polystyrene were varied and reports the results of the physical property tests. It is evident that the proportions of polyphenylene ether and polystyrene can be widely varied and still provide a variety of useful thermoplastic products.

                  TABLE XVII                                                       ______________________________________                                         Example       85      86     87    88   Control                                ______________________________________                                         Component A, parts:                                                            PPE           35      30     25    20   0                                      HIPS          0       5      10    15   35                                     Heat distortion                                                                              162     158    150   138  103                                    temperature, °C.                                                        Flow channel, cm.                                                                            41.9    44.5   44.5  54.6 83.8                                   Dynatup impact, joules                                                         Room temperature                                                                             50.2    47.5   54.2  50.2 17.6                                   -29° C.                                                                               62.4    66.4   54.2  47.5 --                                     Izod impact strength,                                                                        694     721    716   342  69.4                                   joules/m.                                                                      Flex. modulus, GPa.                                                                          1.85    1.90   1.91  1.85 1.70                                   Flex. strength, MPa.                                                                         68.3    68.9   68.9  64.8 49.6                                   Tensile strength at yield,                                                                   46.2    49.0   45.5  48.3 29.6                                   MPa.                                                                           Tensile elongation, parts                                                                    33      30     43    36   8                                      ______________________________________                                    

EXAMPLES 89-96

A series of compositions not containing impact modifiers was prepared by tumble mixing the ingredients in a jar mill and extruding at 265° C. on a twin screw extruder with a screw speed of 400 rpm. The extrudate was quenched in water and pelletized, and the pellets were injection molded into test bars.

The relevant parameters are given in Table XVIII.

                  TABLE XVIII                                                      ______________________________________                                         Example     89    90    91   92   93   94   95  96                             ______________________________________                                         Component A, parts:                                                            PPE         40    45    25   --   --   --   --  --                             PPE-VV      --    --    --   19.8 19.8 47.5 45  42.5                           Component; B, parts:                                                           PBT         40    45    --   66.8 66.8 47.5 45  42.5                           PBT-ES      --    --    33.3 --   --   --   --  --                             Component C, parts:                                                            PC(50,000)  20    10    41.7 13.4 --   --   --  --                             PC(71,000)  --    --    --   --   --   5.0  10  15.0                           PPE-PC      --    --    --   --   13.4 --   --  --                             ______________________________________                                    

EXAMPLES 97-106

The procedure of Examples 89-96 was repeated, using various other combinations of ingredients. In Examples 101-104, conventional antioxidants were also present in effective amounts.

The relevant parameters and test results are given in Table XIX, in comparison with a control containing no polycarbonate.

                                      TABLE XIX                                    __________________________________________________________________________     Example       97 98 99 100                                                                               101                                                                               102                                                                               103                                                                               104 105                                                                               106                                                                               Control                           __________________________________________________________________________     Component A, parts                                                             PPE           -- -- -- -- -- -- -- --  21.4                                                                              21.4                                                                              --                                PPE-VV        -- -- -- -- 34.9                                                                              44 34.9                                                                              20  -- -- 60.5                              Example 2     45.5                                                                              19.8                                                                              19.8                                                                              -- -- -- -- --  -- -- --                                Example 5     -- -- -- 45.8                                                                              -- -- -- --  -- -- --                                HIPS          -- -- -- -- -- -- -- --  14.3                                                                              14.3                                                                              --                                Component B, parts                                                             PBI           45.5                                                                              66.8                                                                              66.8                                                                              45.8                                                                              53.5                                                                              46 53.5                                                                              71  28.6                                                                              -- 39.5                              PBI-ES        -- -- -- -- -- -- -- --  -- 28.6                                                                              --                                Component C, parts                                                             PC(50,000)     9.0                                                                              13.4                                                                              --  8.4                                                                              -- -- -- --  35.7                                                                              35.7                                                                              --                                PC(71,000)    -- -- -- -- 11.6                                                                              10 11.6                                                                              9   -- -- --                                PC(192,000)   -- -- 13.4                                                                              -- -- -- -- --  -- -- --                                Component E: TGIC, parts                                                                     -- -- --  0.5                                                                              -- -- -- --                                          Tensile strength, MPa.:                                                        At yield      -- -- -- -- -- -- 56.6                                                                              52.7                                                                               -- --  4.1                              At break      -- -- -- -- -- -- 40.3                                                                              35.4                                                                               -- -- 26.9                              Tensile elongation, %                                                                        -- -- -- -- -- -- 50 185 -- -- 5                                 __________________________________________________________________________ 

What is claimed is:
 1. A resinous composition comprising:(A) about 15-50% of at least one polyphenylene ether, or a blend thereof with at least one polystyrene, said polyphenylene ether comprising structural units having the formula ##STR9## wherein in each of said units independently, each Q¹ is independently halogen, primary or secondary lower alkyl, phenyl, haloalkyl, aminoalkyl, hydrocarbonoxy, or halohydrocarbonoxy wherein at least two carbon atoms separate the halogen and oxygen atoms, and each Q² is independently hydrogen, halogen, primary or secondary lower alkyl, phenyl, haloalkyl, hydrocarbonoxy or halohydrocarbonoxy as defined or grafted or coupled derivatives thereof; (B) about 20-80% of at least one poly(alkylene dicarboxylate), the weight ratio of component A to component B being at most 1.2:1; and (C) from 3% to about 50% of at least one polymer containing a substantial proportion of aromatic polycarbonate units and having a weight average molecular weight of at least about 40,000 as determined by gel permeation chromatography relative to polystyrene, or a blend thereof with a styrene homopolymer; all percentages being by weight and based on total components A, B and C.
 2. A composition according to claim 1 wherein component A is a blend of a poly(2,6-dimethyl-1,4-phenylene ether) with said polystyrene.
 3. A composition according to claim 2 wherein the polystyrene in component A is a homopolymer.
 4. A composition according to claim 2 wherein the polystyrene in component A is a rubber-modified polystyrene.
 5. A composition according to claim 1 wherein component A is a poly(2,6-dimethyl-1,4-phenylene ether).
 6. A composition according to claim 5 wherein component B is a poly(ethylene terephthalate) or a poly(butylene terephthalate) and the polycarbonate units in component C are bisphenol A polycarbonate units.
 7. A composition according to claim 6 wherein component B is a poly(butylene terephthalate) having a number average molecular weight in the range of about 20,000-70,000.
 8. A composition according to claim 7 wherein component C is a polycarbonate homopolymer having a weight average molecular weight inthe range of about 40,000-80,000.
 9. A composition according to claim 6 wherein the polyphenylene ether contains no more than 800 ppm. of unneutralized amino nitrogen and has an intrinsic viscosity of at least 0.25 dl/g/ as measured in chloroform at 25° C.
 10. A composition according to claim 9 wherein the polyphenylene ether has been prepared by oxidative coupling of at least one monohydroxyaromatic compound in the presence of a catalyst comprising a combination of cuprous or cupric ions, halide and at least one amine.
 11. A composition according to claim 9 wherein component C is a polycarbonate homopolymer having a weight average molecular weight in the range of about 71,000-200,000. 